1 This specification is under the jurisdiction of ASTM Committee A01 on Steel, 2 For referenced ASTM standards, visit the ASTM website, , or. ASTM Aa(). Standard Specification for Tool Steel High Speed. standard by ASTM International, 03/01/ View all product details. Most Recent. ASTM A Standard Specification for High Speed Tool Steel.

Author: Brazilkree Faugal
Country: Laos
Language: English (Spanish)
Genre: Video
Published (Last): 23 January 2018
Pages: 243
PDF File Size: 8.61 Mb
ePub File Size: 9.58 Mb
ISBN: 371-6-96822-424-9
Downloads: 55650
Price: Free* [*Free Regsitration Required]
Uploader: Kijar

Two intermediate high speed tool steels designated as M50 ast M52 are also covered. See “Forging” and consult the supplier for information on working at lower temperatures.

ASTM A600 1992 Standard Specification for High Speed Tool Steel

Selection will depend upon design, service conditions, and mechanical properties. Link to Active This link will always route to the current Active version of the standard. Historical Version s – view previous versions of standard.

It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application. Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard.

  CODUL OCUPATIILOR DIN ROMANIA 2011 PDF

Distributors will offer small quantity buys while mills will generally only sell large quantities, with delivery times anywhere from 10 to 50 weeks depending on size and form required This material is stocked primarily in Bar Products by 28 distributors but is also available to a lesser extent in Flat Rolled Products, Wire Products, and Shapes.

This abstract is a brief summary of the referenced standard.

ASTM A – 92a() Standard Specification for Tool Steel High Speed

M2 is classified as a “medium” machinability tool steel in the annealed condition. Forge at F down to F.

It may be shaped by grinding but is relatively poor in regard to capability of being ground. Primarily used for cutting tools. A chemical analysis of each heat of steel shall be made to determine the percentage of the elements specified including carbon, manganese, phosphorus, sulfur, silicon, chromium, vanadium, tungsten, molybdenum, and cobalt and these values shall conform to the requirements as to the prescribed chemical composition. Consult the alloy supplier for information on the advisability of welding.

See “Heat Treatment” and “Tempering”. Temper at F for a hardness of Rockwell C 60 to ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date.

  FATHER SERGIUS TOLSTOY PDF

M2 Tool Steels Material Property Data Sheet – Product availability and request a quote

Hardens by heat treatment and quenching. Unless otherwise specified, material shall be made by an electric melting process.

Not applicable to this alloy. Then heat rapidly from F to F and hold for 3 to 5 minutes followed by quenching in oil, air or salt bath.

The maximum Brinell hardness and minimum Rockwell C hardness for the tool steels are given. Preheat at F before heating for hardening. Cold working may be accomplished with the alloy in the annealed condition.

Modulus of Elasticity Tension. Do Not forge below F. Formed by machining or forging and then machining. Anneal at F and slow furnace cool at 40 F per hour, or less.

The M2 alloy has somewhat better wear resistance than M1. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.